Welding edge cracks?

profile picture
albinoboy
Posts: 372 - Karma: 2,103
Has anyone tried it? If so what filler wire would work best?

I just ordered a mig welder for home improvement and car work, I don't see why it couldn't work for skis too.
Jan 10 2021 8:18PM
5 0
profile picture
MaimHelp
Posts: 1721 - Karma: 13,579
THE-Albino*Has anyone tried it? If so what filler wire would work best?

I just ordered a mig welder for home improvement and car work, I don't see why it couldn't work for skis too.


Interesting and never thought about it but I’d think it would melt your base perhaps and ruin it or the core or something like that
Jan 10 2021 8:31PM
21 0
profile picture
albinoboy
Posts: 372 - Karma: 2,103
MaimHelpInteresting and never thought about it but I’d think it would melt your base perhaps and ruin it or the core or something like that


sounds about right, Ill do it to some junk skis first and report back my findings.
Jan 10 2021 10:28PM
14 0
profile picture
drifts
Posts: 591 - Karma: 4,340
I dont think a mig has the accuracy to do a ski edge, you could probably tig it with a super fine electrode and no filler rod
Jan 11 2021 1:19AM
12 0
profile picture
BradFiAusNzCoCa
Posts: 6975 - Karma: 60,923
Lol you wilding
Jan 11 2021 5:31AM
4 0
profile picture
RoxanBilli
Posts: 1 - Karma: 10
Because welding for skis is something else entirely
Jun 4 2021 4:21AM
0 0
profile picture
mrk127
Posts: 1803 - Karma: 16,312
I was talking to my welding instructor about this a while back. Edges are stainless so you would have to TIG weld but we concluded that you would catch your ski on fire before you got the stainless hot enough to fuse back together. Stainless has a melting point of like 3000F or so.
Jun 8 2021 1:06AM
6 0
profile picture
a_burger
Posts: 5235 - Karma: 20,715
friend tried this in the shop at the local hill with his old on3ps, pretty sure he said it came back apart the same day.
Jun 8 2021 9:29PM
2 0
profile picture
dolanslebensraum
Posts: 5959 - Karma: -13,099
Get next yrs head oblivions. They are going to have thick edges like on3p
Jun 9 2021 1:18AM
0 7
profile picture
mrk127
Posts: 1803 - Karma: 16,312
DolansLebensraumGet next yrs head oblivions. They are going to have thick edges like on3p

You only say get heads cuz you jizz yourself over race bases
Jun 9 2021 1:27AM
5 0
profile picture
dolanslebensraum
Posts: 5959 - Karma: -13,099
mrk127cuz you jizz yourself over race bases

There hath nigh by happenstance come into being, a race bace that unto dolan be it not jizzed upon fervently.
Jun 9 2021 2:28AM
8 0
profile picture
dolanslebensraum
Posts: 5959 - Karma: -13,099
DolansLebensraumThere hath nigh by happenstance come into being, a race bace that unto dolan be it not jizzed upon fervently.

In other words, yeah i jizz on race bases come at me bro. Ill wax the hair off your mangina bra
Jun 9 2021 2:30AM
3 1
profile picture
mrk127
Posts: 1803 - Karma: 16,312
DolansLebensraumIn other words, yeah i jizz on race bases come at me bro. Ill wax the hair off your mangina bra


Have you ever ever actually jizzed on a race ski and waxed over it tho? Deadass did that shit once and won my race. My skis were running faster than illegal fluoros
Jun 9 2021 3:49AM
9 0
profile picture
weastcoat
Posts: 6419 - Karma: 74,054
Just put epoxy in it and file her down
Jun 10 2021 11:12PM
3 0
profile picture
CharlzHub
Posts: 1165 - Karma: 8,537
mrk127I was talking to my welding instructor about this a while back. Edges are stainless so you would have to TIG weld but we concluded that you would catch your ski on fire before you got the stainless hot enough to fuse back together. Stainless has a melting point of like 3000F or so.


Surely you could just do a quick tack and then blow out the flames straight away
Jun 16 2021 11:36PM
1 0
profile picture
anders_a
Posts: 1680 - Karma: 5,603
I've been wanting to try it, but have no cracked skis currently! I'd use TIG, but MIG should work
Jun 17 2021 2:53PM
1 0
profile picture
dolanslebensraum
Posts: 5959 - Karma: -13,099
DolansLebensraumThere hath nigh by happenstance come into being, a race bace that unto dolan be it not jizzed upon fervently.


Jun 17 2021 8:11PM
1 1
profile picture
mrk127
Posts: 1803 - Karma: 16,312
bumping, Has anyone tried or know about spot welding edge cracks? obviously normal welding TIG/MIG puts way too much heat into the ski. So I'm thinking spot welding wouldn't put too much heat into that It would damage the ski/sidewall. But idk if spot welding would actually cause enough fusion to make a difference. input?
Nov 14 2021 11:56PM
1 0
profile picture
oldmanski
Posts: 3311 - Karma: 23,801
Hmmm. Like others have said, TIG would be ideal for this as MIG would cause more damage to the ski/base.
I almost wonder if solder would work. You may be able to heat the metal up enough to allow solder to fill the crack. Cant say I have tried this on a ski edge but I have soldered metal cracks on other items. Its like a form of brazing with lead. Hot enough iron you should be able to melt the material into the crack and file down. You also may be able to just braze it too, use a torch and heat the metal up and then melt the lead into the crack. Just dont melt the base of the ski with the torch. Good luck.
Nov 15 2021 7:31AM
0 0
profile picture
tominiemenmaa
Posts: 573 - Karma: 3,387
Installing molten metal into a construction of plastic and wood. What could possibly go wrong?
Nov 16 2021 3:43AM
2 0
profile picture
mrk127
Posts: 1803 - Karma: 16,312
tominiemenmaaInstalling molten metal into a construction of plastic and wood. What could possibly go wrong?

That’s why I’m saying spot welding might work. No filler added and low heat
Nov 16 2021 4:55AM
0 0
profile picture
tominiemenmaa
Posts: 573 - Karma: 3,387
Spot welding wont do anything else but make the edges harder = brittler. Not gonna work.
mrk127That’s why I’m saying spot welding might work. No filler added and low heat
Nov 16 2021 6:15AM
0 0
profile picture
albinoboy
Posts: 372 - Karma: 2,103
oldmanskiHmmm. I almost wonder if solder would work. You may be able to heat the metal up enough to allow solder to fill the crack. Cant say I have tried this on a ski edge but I have soldered metal cracks on other items. Its like a form of brazing with lead. Hot enough iron you should be able to melt the material into the crack and file down.

I soldered some cracks last season. wasn't able to get hot enough to fuse the whole crack but the underside where I did it held up through most of the season. Maybe adding a slight bevel between the cracks could allow for filling and better penetration?
Nov 16 2021 8:04PM
1 0
profile picture
dolanslebensraum
Posts: 5959 - Karma: -13,099
Get oblivions
Nov 16 2021 9:44PM
0 0
profile picture
oldmanski
Posts: 3311 - Karma: 23,801
THE-Albino*I soldered some cracks last season. wasn't able to get hot enough to fuse the whole crack but the underside where I did it held up through most of the season. Maybe adding a slight bevel between the cracks could allow for filling and better penetration?


It wouldnt hurt any to give it a try. The edge is already cracked.
I think @weastcoat said the best option really, epoxy them and file down.
Nov 17 2021 3:23AM
1 0